| No. |
Performance Parameter |
Test Standard |
Industry Required Index |
BIDE TPU Floor Tested Index |
Core Advantage |
| 1 |
Shore A Hardness |
GB/T 2411-2008 |
≥85 |
91 |
Meets hardness standard, balances elasticity and wear resistance |
| 2 |
Tensile Strength |
GB/T 528-2009 |
≥8.0 MPa |
15.3 MPa |
Far exceeds industry requirements, excellent tensile and deformation resistance |
| 3 |
Chemical Resistance |
BS EN ISO 26987-2012 |
No surface change |
No surface change |
Acid, alkali and oil resistant, suitable for complex environments |
| 4 |
Cold Resistance |
TB/T 3138-2018 |
No crack at -25℃ |
No crack at -25℃ |
No brittleness at low temperature, suitable for extreme climates |
| 5 |
Cigarette Burn Resistance |
EN 1399-1997 Method A |
≥Grade 3 |
Grade 4 |
Flame retardant and burn resistant, far exceeds industry safety standards |
| 6 |
Slip Resistance |
DIN 51130-2014 |
≥Grade R10 |
Grade R10 |
Meets slip resistance standard, ensures walking safety in wet and dry environments |
| 7 |
Dimensional Stability |
ISO23999-2018 |
≤0.2% |
0.20% |
Extremely low dimensional change rate, no shrinkage or deformation after long-term use |
| 8 |
Wear Resistance |
BS ISO 9352-2012 |
≤400mg |
1.3mg |
Wear resistance far exceeds industry requirements, greatly extends service life |
| 9 |
Thickness Tolerance |
GB/T6342-1996 |
±0.25mm |
±0.2mm |
More precise thickness control, higher installation fit |
| 10 |
Chair Castor Resistance |
BS EN 425-2002 |
No obvious surface change or scratch |
No obvious surface change or scratch |
Rolling and scratch resistant, suitable for high-frequency use scenarios |
| 11 |
Light Fastness |
EN ISO 105-B02-2014 |
≥Grade 3 |
Grade 4-5 |
UV resistant, not easy to fade, stable appearance after long-term use |
| 12 |
Flex Resistance |
BS EN ISO 24344-2012 Procedure A |
Bending diameter 20mm |
Bending diameter 20mm |
Excellent flexibility, suitable for complex curved surface installation |
| 13 |
Residual Indentation |
ISO24343-1-2007 |
≤0.2mm |
0.09mm |
Excellent depression resistance and resilience, quickly recovers after heavy load |
| 14 |
Internal Peel Strength |
BS EN ISO 24345-2012 |
≥1 N/mm |
3.7 N/mm |
High structural strength, not easy to delaminate or warp |
| 15 |
Anti-static Property |
EN 1815-1997 |
≤2KV |
0.1KV |
Excellent anti-static performance, suitable for rail transit, electronic workshop and other special scenarios |
| 16 |
Footstep Noise Absorption |
GB/T 19889.3-2005 |
≥6dB |
24dB |
Noise reduction effect far exceeds industry requirements, greatly improves walking comfort |
| 17 |
Tear Resistance |
GB/T 529-2008 |
≥60kN/m |
70kN/m |
Tear and damage resistant, more durable |
| 18 |
Environmental Protection (Heavy Metals) |
TB/T3139 |
Soluble lead ≤20mg/m²Soluble cadmium ≤20mg/m² |
Soluble lead: Not Detected (N.D.)Soluble cadmium: Not Detected (N.D.) |
No harmful heavy metals, fully meets rail vehicle environmental safety standards |
| 19 |
Environmental Protection (Volatiles) |
TB/T3139 |
Volatiles ≤35g/m2 |
Volatiles: 2g/m² |
Extremely low volatilization, no odor, green and environmentally friendly |
| 20 |
TVOC & Formaldehyde |
TCF00000222499ISO16000-6 |
Formaldehyde ≤0.02mg/m³TVOC ≤1.8mg/m³ |
Formaldehyde: Not Detected (N.D.)TVOC: 0.15&0.181mg/m³ |
Formaldehyde-free, extremely low TVOC, far exceeds indoor/vehicle air quality safety standards |